99.5%Min ZnO for Ceramics Light Yellow CAS1314-13-2 Calcined Zinc Oxide

• Customization: Available
• CAS No.: 1314-13-2
• Formula: ZnO
• Model NO.: 99.5%min
• EINECS: 215-222-5
• Classification: Zinc Oxide
• Grade Standard: Industrial Grade
• Kind: Amphoteric Oxide
• Quality: First Class
• Molecular Weight: 81.38
• Melting Point: 1975
• Boiling Point: 2360
• Dendity: 5.606g/cm3
• Solubility: Unsoluble in Water
• Flash Point: 1436
• Acid-Base Property: Both But Meta Alkalescence
• Usage: for Plastic, Ceramics, Glass, Cement
• Sample: Availiable
• Transport Package: 25/50/1000kg Bag Packing
• Specification: 99.5%Min
• Trademark: Fitech
• Origin: China
• HS Code: 2817001000
• Production Capacity: 1000mt/Year

Product Description

Zinc Oxide

1. Molecular formula: Zinc Oxide

2. Purity: 99.5%min

3. CAS: 1314-13-2

4. HS Code: 2817001000
 

5. Melting Point: 1975ºC
    In order to improve the physical properties and chemical composition of raw zinc oxide extracted by zinc steam, such as direct zinc oxide and indirect zinc oxide, on ceramic glaze, heavy zinc oxide was prepared by high temperature processing and calcination.
    Calcined zinc oxide ratio is significant, good fluidity, with its production of glaze shrinkage is small, the glaze is not easy to pinhole and crack. The quality standard of calcined zinc oxide is the same as that of grade zinc oxide except for the ratio.
After calcined at high temperature, zinc oxide shows light yellow and its melting point is 1975ºC.

Product name	Zinc Oxide
Grade	Industrial Grade
Color	Light Yellow
Purity	99.5%min
Shape	Powder
Density	5.606 g/cm³
Melting Point	1975ºC

Applications

1. Used as flux: when ZnO is used as flux in low-temperature frit glaze, the general dosage is between 5% and 10%, and about 5% in low-temperature raw glaze.

2. Used as opacification agent: Zinc oxide was added to glazing with high Al2O3 to improve opacification of glazing. Because ZnO can form zinc spinel crystals with Al2O3. In zinc-containing opacities glazes, Al2O3 can improve the whiteness and opacities of glazes. SiO2 can improve the gloss of the glaze.

3. Used as crystallization agent: in the art glaze crystal glaze, ZnO is indispensable crystallization agent, in the molten
glaze cooling, it forms a large crystal pattern, very beautiful. The amount of ZnO in crystalline glaze is up to 20 ~ 30%.

4. To make cobalt blue glaze: ZnO is a very important flux in cobalt blue glaze, it can make cobalt oxide in the glaze to form a beautiful sky blue.

5. Used as ceramic pigments: because of its strong melting effect, ZnO can be used as a flux of ceramic pigments, mineralizing agent and glaze color carrier. Used as main raw material in brown ceramic color series

6. As a glass additive: add aluminum, gallium and nitrogen zinc oxide transparency up to 90%, can be used as a glass coating, let visible light through at the same time reflect infrared. Paint can be applied on the inside or outside of window glass to achieve the effect of heat preservation or insulation.

Related Products

                                                 Nickel Oxide                                                                                                       Bismuth Trioxide

Packing

       Corner of the Factory                                                                                          Factory Environment
 

Q: Are you trading company or manufacturer ?

A: We are factory.

Q: How long is your delivery time?

A: Generally it is 5-10 days if the goods are in stock. or it is 15-20 days if the goods are not in stock, it is according to quantity.

Q: Do you provide samples ? is it free or extra ?

A: Yes, we could offer the sample for free charge but do not pay the cost of freight.

Q: What is your terms of payment ?

A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 30% T/T in advance ,balance before shippment.