| Customization: | Available |
|---|---|
| CAS No.: | 1332-37-2 |
| Formula: | Fe2o3 |
|
Still deciding? Get samples of US$ 40/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Features
Iron oxide pigment Feature:
Compound Ferric Green:
| Fe2O3 or Fe3O4 (%) | - |
| Oil absorption (ml/100g) | 25-35 |
| Res.on325 mesh (%) | ≤0.3 |
| Water sol.Salts (%) | ≤2.0 |
| Moisture | ≤1.0 |
| PH value | ≥6.0 |
| Tamped apparent density (g/cm3) | 0.4-0.8 |
| Particle shape | irregular |
| Compared with std. | ≤1 |
| Tinting strength | 95-105 |
Orange 960:
| Fe2O3 or Fe3O4 (%) | ≥88 |
| Oil absorption (ml/100g) | 20-30 |
| Res.on325 mesh (%) | ≤0.3 |
| Water sol.Salts (%) | ≤0.3 |
| Moisture | ≤1.0 |
| PH value | 3-7 |
| Tamped apparent density (g/cm3) | 0.4-0.6 |
| Particle shape | irregular |
| Compared with std. | ≤1 |
| Tinting strength | 95-105 |
Application
Iron oxide pigment on rubber and plastic application, with no contain copper, manganese and other heavy metal ion, iron oxide red can be used for aviation tires and prevent aging rubber. Iron oxide pigments with strong tighting strength, pure color characteristics, as a coloring agent and a filler used in PVC plastic flooring, PVC colored film, thermosetting plastics in a jade powder, bakelite powder, and polyolefins thermoplastics can be used, iron oxide pigment also can make into master batch or slurry preparation, now become very popular in plastic industry.
Iron oxide pigments use on RUBBER:
after the raw rubber is generally washed and purified with the necessary mechanical treatment of the plasticity of the rubber, then adding a vulcanizing agent and iron oxide pigments, zinc oxide, calcium carbonate filler is controlled to obtain raw rubber blanks. Various rubber molded products reprocessed parts.
Iron oxide pigment use on PLASTIC:
products such as the use of asbestos in brake plastic board, whichever resin, asbestos, iron oxide pigments are mixed together, in order to adjust the viscosity of the solvent must be kneaded and dried, then put plastic take asbestos I in the press molding, decorative wood paper Serve coloring process iron oxide pigments for PVC: the first step iron oxide pigments and plasticizers (phthalate esters zinc ') mixed into a thick paste ( The amount of oil absorption size divided by 2: 1,1 1.1, l: o.5 etc.), put in a flat roll or three-roll grinding machine (with a transparent film and the opaque film), then in accordance with transparent or opaque film formulation each component and paste reconcile even until no color filiform, color point, then granule, his rendering of the polyvinyl chloride paste was filled in the applicator, the flow uniformly coated on a glass plate, to be still, to drain, after defoaming. Placed in an oven at 180 ??C blower, plasticized, taken out to cool for 10 minutes, Serve colorless or colored PVC film.