Customization: | Available |
---|---|
Type: | Alloy Steel Powder |
Standard: | AISI, ASTM, GB |
Still deciding? Get samples of US$ 15/kg
Request Sample
|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Features
The use of 420 die steel quenching and tempering state (hardness 48-54HRC), in order to meet the long-term work or the number of parts up to 1 million or more life requirements, the more suitable use method should be quenching low temperature tempering treatment. Quenching is first heated to 1000-1050ºC to hold heat for a certain time (calculated at 30 minutes /25mm), and then quenched into the oil to cool to 50-100ºC and immediately temper treatment to prevent cracking. Tempering at 200ºC (at least 4 hours) hardness can reach more than 48HRC, with better polishing and better corrosion resistance.
Main products |
420 |
|||
mobility |
15-53μm |
≤18s/50g |
||
Bulk density |
≥4.10g/cm3 |
|||
Oxygen content |
≤300ppm |
|||
Nitrogen content |
≤300ppm |
|||
Mechanical property |
Compressive strength /MPa 1750±50 Yield strength /MPa 1450±50 Elongation /% 6±2 |